Structural and Chemical Evolution of the SOFC Anode La0.30Sr0.70Fe0.70Cr0.30O3−δ upon Reduction and Oxidation: An in Situ Neutron Diffraction Study
Although some perovskite oxides have been shown to be stable solid oxide fuel cell (SOFC) anodes, the actual crystal structure of these materials under operating conditions is largely unknown. In this paper, the structural evolution of the SOFC anode La0.30Sr0.70Fe0.70Cr0.30O3−δ was studied at 800 a...
Saved in:
Published in: | Chemistry of materials 2010-05, Vol.22 (10), p.3283-3289 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Although some perovskite oxides have been shown to be stable solid oxide fuel cell (SOFC) anodes, the actual crystal structure of these materials under operating conditions is largely unknown. In this paper, the structural evolution of the SOFC anode La0.30Sr0.70Fe0.70Cr0.30O3−δ was studied at 800 and 900 °C (similar to SOFC operating temperatures) in progressively reducing and oxidizing environments. The perovskite was shown to be stable down to a pO2 of 10−20 atm at 800 °C and a pO2 of 10−18 atm at 900 °C, at which point a spinel phase formed. Further reduction led to the formation of Fe metal. The phase separation of La0.30Sr0.70Fe0.70Cr0.30O3−δ was also shown to be completely reversible with an increase in the partial oxygen pressure and reoxidation of the sample. |
---|---|