PROPRIEDADES DE PAINÉIS AGLOMERADOS SUBMETIDOS AO TRATAMENTO TÉRMICO
The particleboards are the most consumed in the world, where much of the demand is associated to furniture sector. This study aims to assess the heat treatment effect on particleboard panels. The experiment consisted of four treatments and the control sample, evaluating temperatures of 160°C and 180...
Saved in:
Published in: | Ciência florestal 2019-02, Vol.28 (2) |
---|---|
Main Authors: | , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The particleboards are the most consumed in the world, where much of
the demand is associated to furniture sector. This study aims to assess
the heat treatment effect on particleboard panels. The experiment
consisted of four treatments and the control sample, evaluating
temperatures of 160°C and 180°C for six and twelve minutes.
Commercial particleboard panels were produced with particles of
Eucalyptus sp. and urea-formaldehyde synthetic resin. Samples for
physical testing (water absorption, and thickness swelling) and
mechanical (static bending strength and screw withdrawal strength) were
taken from these panels. For physical properties, the assessed heat
treatments influenced significantly the water absorption of the panels
after 24 hours of immersion. The treatment that utilized temperature of
180°C for six minutes provided the best performance. Concerning to
the mechanical properties, the evaluated treatments had
non-significantly influence in the panels strength.
Os painéis aglomerados são os mais consumidos no mundo, sendo
que grande parte da demanda destes painéis está associada ao
setor moveleiro. O presente estudo teve como objetivo avaliar o efeito
do tratamento térmico em painéis aglomerados. O experimento
consistiu de quatro tratamentos mais a testemunha, avaliando as
temperaturas de 160 e 180°C por períodos de seis e doze
minutos. Foram utilizados painéis aglomerados comerciais
produzidos com partículas de Eucalyptus sp. e, resina
sintética ureia-formaldeído. Destes painéis foram
retiradas amostras para os ensaios físicos (absorção de
água e inchamento em espessura) e mecânicos (resistência
à flexão estática e resistência ao arrancamento de
parafuso). Para as propriedades físicas, os tratamentos
térmicos avaliados influenciaram significativamente a
absorção de água dos painéis após 24 horas de
imersão. O tratamento que utilizou a temperatura de 180°C por
seis minutos foi o que proporcionou o melhor desempenho. Já para
as propriedades mecânicas, os tratamentos avaliados não
influenciaram significativamente a resistência dos painéis. |
---|---|