Preparation and Characterization of Gd3 Sc2 Ga3 O12 Polycrystalline Material by Co-Precipitation Method

Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered at various temperatures were characterized by infrared spectra （IR）, X-ray diffracto...

Full description

Saved in:
Bibliographic Details
Published in:Journal of rare earths 2007, Vol.25 (2), p.158-162
Main Author: 邵淑芳 张庆礼 苏静 孙敦陆 王召兵 殷绍唐
Format: Article
Language:English
Subjects:
Gd3Sc2Ga3O12
共沉淀法
多晶材料
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Gd3Sc2Ga3O12 polycrystalline material for single crystal growth was prepared with Ga, Gd2O3 and Sc2O3 as starting materials and aqueous ammonia as the precipitator by co-precipitation method. The precursors sintered at various temperatures were characterized by infrared spectra （IR）, X-ray diffractometry （XRD） and transmitted electron microscopy （TEM）. The results showed that pure GSGG phase could be obtained at 900 ℃. The sintered powders were well-dispersed and less-aggregated in the sintered temperature range of 900 - 1000 ℃. XRD and TEM show that the polycrystalline particle sizes of the polycrystalline powders were about 20 - 50 nm. Compared with the method that Ga2O3, Gd2O3 and Sc2O3 were mixed directly and sintered to get polycrystalline materials, the synthesized temperature was lower and sintered time was shorter. Thus co-precipitation was a good method to synthesize GSGG polycrystalline material.
ISSN:1002-0721
2509-4963