Structure and Luminescent Properties of Sm^3+ Doped SrO-MgO-SiO2 Glass Ceramics

A new type of samarium ion activated luminescent glass ceramics with main crystal phase of melilite was prepared. The effect of heat-treatment temperature on the structure of glass ceramics was investigated by X-ray diffraction analysis(XRD), scanning electron microscope(SEM) and fluorescence spectr...

Full description

Saved in:
Bibliographic Details
Published in:武汉理工大学学报:材料科学英文版 2015 (2), p.282-287
Main Author: ZHANG Luxian HE Feng XIE Junlin LIU Jia
Format: Article
Language:English
Subjects:
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A new type of samarium ion activated luminescent glass ceramics with main crystal phase of melilite was prepared. The effect of heat-treatment temperature on the structure of glass ceramics was investigated by X-ray diffraction analysis(XRD), scanning electron microscope(SEM) and fluorescence spectrometer. In the Sm^3+ doped SrO-MgO-SiO2 glass ceramic, its excitation spectra are in the wavelength range of 350-500 nm, and its excitation peaks are at 360 nm, 374 nm, 404 nm, 417 nm, and 475 nm with the host excitation peak of 404 nm, showing a strong orange-red luminescence when using 404 nm violet to excite it, and its emission peaks are at 564 nm, 600 nm and 648 nm with the host emission peak at 600 nm. The increase in the heat-treatment temperature has no infl uence on the position of the fl uorescent spectra. However, with the increase of heat-treatment temperature, the intensity of fl uorescence spectrum shows an increasing tendency. The increase in the concentration of Sm3+ also improves the intensity of the fl uorescent spectra. In the experimental concentration range(0.05mol%-0.30mol%), a special concentration quenching phenomenon happens.