Wear Resistances of CO_2 Corrosion Product Films in the Presence of Sand Particles

Wear resistances of CO2 corrosion product films formed on P110 carbon steel at different CO2 partial pressures were investigated in water sand two-phase flow by weight loss method, and the microstructures and compositions of corrosion product films were analyzed by scanning electron microscope（SEM）...

Full description

Saved in:
Bibliographic Details
Published in:武汉理工大学学报：材料科学英文版 2015 (5), p.968-973
Main Author: LI Jinling ZHU Shidong LIU Luzhen QU Chengtun YAN Yongli YANG Bo
Format: Article
Language:English
Subjects:
carbon
corrosion
diffraction
electron
microscope
product
scanning
steel
wear
X-ray
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Wear resistances of CO2 corrosion product films formed on P110 carbon steel at different CO2 partial pressures were investigated in water sand two-phase flow by weight loss method, and the microstructures and compositions of corrosion product films were analyzed by scanning electron microscope（SEM） and X-ray diffraction（XRD）, respectively. The results showed that the wear rate of CO2 corrosion product films increased until a maximum and then decreased with the increasing of the film-forming pressure, and the maximum occurred at 2 MPa. However, the maximal corrosion rate and the loose and porous CO2 corrosion product films were obtained at 4 MPa. And the wear rate decreased and then went to be flat with increasing test time. Furthermore, the microstructures and compositions of corrosion product films and the impact and wear of sand particles played an important role on wear resistances. In addition, the wear rate and corrosion rate were fitted by cubic polynomial, respectively, which were well in accordance with the measured results.
ISSN:1000-2413
1993-0437