Catalytic performance of a Pt-Rh/CeO_2-ZrO_2-La_2O_3-Nd_2O_3 three-way compress nature gas catalyst prepared by a modified double-solvent method

• Published in: 中国稀土学报：英文版 2017, Vol.35 (9), p.857-866
• Main Author: 陈建军 胡伟 黄福进 李广霞 袁山东 龚茂初 钟琳 陈耀强
• Format: Article
• Language: English
• Subjects: XPS分析; X射线光电子能谱; 催化剂改性; 催化性能; 制备; 压缩天然气; 双溶剂法; 过时效处理
• ISSN: 1002-0721; 2509-4963

A Pt-Rh three-way catalyst（M-DS） supported on CeO_2-ZrO_2-La_2O_3-Nd_2O_3 and its analogous supported catalyst（DS） were developed via a modified double-solvent method and conventional double-solvent method, respectively. The as-prepared catalysts were characterized by N_2 adsorption-desorption, X-ray diffraction（XRD）, CO-chemisorption, X-ray photoelectron spectroscopy（XPS） and hydrogen temperature-programmed reduction（H_2-TPR）. The preformed Pt nanoparticles generated using ethanol as a reducing agent on M-DS presented enhanced Pt dispersion regardless of aging treatment as confirmed by XRD and CO-chemisorption measurements. The textural properties and reduction ability of M-DS were maintained to a large extent after aging treatment. This result was consistent with those of the N_2 adsorption-desorption and H_2-TPR, respectively. Meanwhile, the XPS analysis demonstrated that higher Pt~0 species and larger Ce~（3＋） concentration could be obtained for M-DS. In the conversion of a simulated compressed natural gas（CNG） vehicle exhaust, both fresh and aged M-DS showed a significant enhancement in the activity and N_2-selectivity. Particularly, the complete conversion temperature（T_（90）） of CH_4 over the aged M-DS catalyst was 65 oC lower than that over the aged catalyst by conventional double-solvent method.