An ATR-FTIR study on penetration of resins in wood

• Published in: Die Angewandte makromolekulare Chemie 1992, Vol.200 (1), p.77-92
• Main Authors: Jensen, Eirik S., Gatenholm, Paul, Sellitti, Claudio
• Format: Article
• Language: English
• ISSN: 0003-3146; 1522-9505
• DOI: 10.1002/apmc.1992.052000107

Wood samples were treated with allylic ether resins having various molecular weights, various structures and with the use of different solvents. Using a technique based on Attenuated Total Reflectance Fourier Transform Infrared Spectroscopy (ATR‐FTIR), differences in the characteristic bands of wood and resin were monitored throughout a piece of wood treated with resins and thus a penetration profile was demonstrated. ATR‐FTIR showed that there were differences in the chemical composition of the wood itself at different depths from the surface. The resins could be detected at a depth of more than 3 mm into the wood after 4 days of penetration by gravity. Using a characteristic band for wood as an internal standard, it could be demonstrated that penetration depends upon the solvent used, molecular weight of the resin and also morphology of the wood. Holzproben wurden mit Allyletherharzen mit verschiedenen Molekulargewichten, unterschiedlichen Strukturen und unter Verwendung verschiedener Lörsungsmittel behandelt. Mit einer auf der ATR‐FTIR‐Spektroskopie beruhenden Methode wurden anhand der Unterschiede in den für Holz und Harz charakteristischen Banden Penetrationsprofile erstellt. Mit dieser Methode konnten Unterschiede in der chemischen Zusammensetzung des Holzes in Abhängigkeit von der Entfernung von der Oberfläche nachgewiesen werden. Die Harze konnten nach 4 Tagen Penetration unter Schwerkraft in mehr als 3 mm Tiefe nachgewiesen werden. Anhand einer für Holz charakteristischen Bande als internem Standard wird gezeigt, daß die Penetration vom Lösungsmittel, vom Molekulargewicht des Harzes und der Struktur des Holzes abhängt.