Living cationic polymerization of isobutyl vinyl ether (II): Photoinduced living cationic polymerization in a mixed solvent of toluene and diethyl ether

A new method of preparation of living cationic polymer of isobutyl vinyl ether via photoinduced polymerization in the presence of diphenyliodonium iodide (DPII, initiator) and zinc iodide in a mixed solvent of toluene/diethyl ether, which was irradiated at −78°C for short period, was completed withi...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied polymer science 2006-09, Vol.101 (6), p.3581-3586
Main Authors: Kwon, Soonhong, Lee, Younsung, Jeon, Hyunjeong, Han, Kyuchan, Mah, Soukil
Format: Article
Language:English
Subjects:
Applied sciences
cationic polymerization
Exact sciences and technology
living polymerization
photopolymerization
Physicochemistry of polymers
poly(vinyl ethers)
Polymerization
Polymers and radiations
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A new method of preparation of living cationic polymer of isobutyl vinyl ether via photoinduced polymerization in the presence of diphenyliodonium iodide (DPII, initiator) and zinc iodide in a mixed solvent of toluene/diethyl ether, which was irradiated at −78°C for short period, was completed within 15 min. The reaction was allowed for further reaction in the dark until monomer was fully consumed. It was found that increase in the conversion of monomer to polymer during the irradiation is very limited. Confirmation of the linear dependence of number‐average molar mass of resulting polymer on % conversion together with the fact that polymerization proceeds until monomer consumption, and controllability of number‐average molar mass of resulting polymer, depending on the molar ratio of monomer and initiator, strongly suggests the living nature of this polymerization, unless reaction temperature becomes higher than 0°C, i.e., the absence of chain breaking process. The narrow molar mass distribution, whose polydispersity index values are less than 1.2, reveals that the rate of initiation where irradiation is usually completed within 15 min is much faster than that of propagation in cationic nature in this system. Effect of some major factors, such as solvent polarity and temperature, on the living nature of the polymerization was also investigated. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 3581–3586, 2006
ISSN:0021-8995
1097-4628
DOI:10.1002/app.22619