The Deuterium attack of titanium electrodes under electric discharge conditions

• Published in: Materials and corrosion 1997-10, Vol.48 (10), p.700-704
• Main Authors: Sannikov, V. I., Averin, S. A., Sulimov, E. M., Chelokh, S. O., Bainova, G. D.
• Format: Article
• Language: English
• ISSN: 0947-5117; 1521-4176
• DOI: 10.1002/maco.19970481006

Electrochemical and electrophysical investigations methods of TiD2, LiD(v)‐LiD(m)‐Me systems with subsequent structure and metallographic testing of the titanium electrodes were carried out. Electrophysical properties of a system depend upon metallic (liquid) cathode emission properties. TiD2 content was shown to be higher in Ti anodes with significant surface changes (nondeep cracks creation) after testing and Ti‐cathodes show deep cracks. The maximal hardened material was observed at the crack creation zone. Deuteriumangriff von Titanelektroden unter elektrischen Entladungsbedingungen Elektrochemische und elektrophysikalische Untersuchungen von TiD2, LiD(v)‐LiD(m)‐Me Systemen mit anschließender metallographischer Beurteilung der Titanelektroden wurden durchgeführt. Die elektrophysikalischen Eigenschaften eines Systems hängen von den metallischen (flüssig) Emissionseigenschaften der Kathode ab. Bei den Ti‐Anoden wurden nach den Versuchen höhere TiD2,‐Gehalte und signifikante Oberflächenveränderungen gefunden, die aber keine tiefe Rißbildung zeigten, während die Ti‐Kathoden tiefe Risse aufwiesen. Der am stärksten aufgehärtete Bereich wurde in der Rißbildungszone beobachtet.