Polymerization of propylene with vanadium halides and aluminum alkyls

• Published in: Die Makromolekulare Chemie 1964, Vol.76 (1), p.54-65
• Main Authors: Natta, G., Mazzanti, G., De Luca, D., Giannini, U., Bandini, F.
• Format: Article
• Language: English
• ISSN: 0025-116X; 0025-116X
• DOI: 10.1002/macp.1964.020760104

The polymerization of propylene with VCl3 and aluminum alkyls has been studied. The decrease of the polymerization rate with the increase of the polymerization temperature, in the presence of the catalytic system VCl3‐Al(C2H5)3, is connected with the surface reduction of VCl3 to VCl2. When using Al(C2H5)2Cl at temperatures below 90°C. no reduction of VCl3 is detectable, and the rate of polymerization regularly increases with increasing temperature. Using VCl3 in combination with Al(C2H5)3 the stereospecificity is higher than in the case of Al(C2H5)2Cl, in contrast to catalytic systems based on violet TiCl3. Die Polymerisation des Propylens mit Mischkatalysatoren aus Vanadiumtrichlorid und aluminiumorganischen Verbindungen wird beschrieben. Der starke Abfall der Aktivität des aus VCl3 und Al(C2H5)3 hergestellten Katalysators mit steigender Temperatur wird mit der an der Oberfläche stattfindenden Reduktion des VCl3 zu VCl2 in Beziehung gesetzt. Verwendet man Al(C2H5)2Cl bei Temperaturen < 90°C, so beobachtet man keine Reduktion des VCl3, aber eine regelmäßige Abnahme der Polymerisationsgeschwindigkeit mit der Temperatur. Im Gegensatz zu Beobachtungen am Katalysatorsystem aus violettem TiCl3 ist die Stereospezifität mit VCl3 höher, wenn man Al(C2H5)3 statt Al(C2H5)2Cl als metallorganische Verbindung verwendet.