One Pot Hydrogenation of Furfural to 2‐Methyl Tetrahydrofuran over Supported Mono‐ and Bi‐metallic Catalysts

2‐Methyltetrahydrofuran is a valuable commercial product that can be obtained by direct hydrogenation of furfural. In the present study, among several carbon supported bimetallic Ir−Ni catalysts with different loadings screened, 4% Ir‐4% Ni/C catalyst showed excellent activity in terms of direct con...

Full description

Saved in:
Bibliographic Details
Published in:ChemistrySelect (Weinheim) 2020-08, Vol.5 (31), p.9590-9600
Main Authors: Date, Nandan S., Hengne, Amol M., Huang, K.‐W., Chikate, Rajeev C., Rode, Chandrashekhar V.
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:2‐Methyltetrahydrofuran is a valuable commercial product that can be obtained by direct hydrogenation of furfural. In the present study, among several carbon supported bimetallic Ir−Ni catalysts with different loadings screened, 4% Ir‐4% Ni/C catalyst showed excellent activity in terms of direct conversion (99%) to 2‐MeTHF with a maximum selectivity of ∼74% at 220 °C and 750 psig, suppressing the formation of side chain as well as ring opening products. The catalytic activity was found to be mainly affected by catalyst preparation methods, metal loadings, surface composition, temperature, pressure and catalyst loading. HR‐TEM and STEM revealed well dispersed Ir−Ni NPs having the particle sizes in the range of 2 to 5 nm. Different phases of Ir i. e. Ir° and IrO2 as well as oxygen vacancies were found to be responsible for hydrogenation of furfural to 2‐methyl furan while, Ni° and NiO were responsible for further hydrogenation to 2‐MeTHF. The synergic effect between Ir and Ni was established through XPS, H2‐TPR analysis. With the help of some control experiments, the plausible reaction pathway was also proposed. The catalyst prepared by co‐impregnation method found more effective than prepared by sequential addition method. At lower Ni loadings of 1% and 2%, low temperature of 160 °C as well as at low H2 pressure of 250 psig, mixture of furfuryl alcohol and 2‐methyl furan were formed selectively. Catalyst could be successfully reused up to 3 times without leaching of metals. Synergic role between iridium and nickel is responsible for high selectivity of 2‐MeTHF (74%) in hydrogenation of furfural.
ISSN:2365-6549
2365-6549
DOI:10.1002/slct.202002322