3D Fast Sodium Transport Network of MoS 2 Endowed by Coupling of Sulfur Vacancies and Sn Doping for Outstanding Sodium Storage

• Published in: Small (Weinheim an der Bergstrasse, Germany) Germany), 2024-05, Vol.20 (21), p.e2309112
• Main Authors: Kang, Jia, Peng, Yan, Zhu, Ling, Tang, Yao, Teng, Feiyang, Guo, Gencai, Xiang, Yanhong, Huang, Yonggang, Wu, Xianming, Wu, Xianwen
• Format: Article
• Language: English
• ISSN: 1613-6810; 1613-6829
• DOI: 10.1002/smll.202309112

A sulfur vacancy-rich, Sn-doped as well as carbon-coated MoS composite (Vs-SMS@C) is rationally synthesized via a simple hydrothermal method combined with ball-milling reduction, which enhances the sodium storage performance. Benefiting from the 3D fast Na transport network composed of the defective carbon coating, Mo─S─C bonds, enlarged interlayer spacing, S-vacancies, and lattice distortion in the composite, the Na storage kinetics is significantly accelerated. As expected, Vs-SMS@C releases an ultrahigh reversible capacity of 1089 mAh g at 0.1 A g , higher than the theoretical capacity. It delivers a satisfactory capacity of 463 mAh g at a high current density of 10 A g , which is the state-of-the-art rate capability compared to other MoS based sodium ion battery anodes to the knowledge. Moreover, a super long-term cycle stability is achieved by Vs-SMS@C, which keeps 91.6% of the initial capacity after 3000 cycles under the current density of 5 A g in the voltage of 0.3-3.0 V. The sodium storage mechanism of Vs-SMS@C is investigated by employing electrochemical methods and ex situ techniques. The synergistic effect between S-vacancies and doped-Sn is evidenced by DFT calculations. This work opens new ideas for seeking excellent metal sulfide anodes.