The relationship between growth forms and the preferred direction of growth

• Published in: Acta metallurgica 1957-01, Vol.5 (10), p.565-573
• Main Authors: Rosenberg, A, Tiller, W.A
• Format: Article
• Language: English
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(57)90124-4

The morphologies of the growth forms associated with the various modes of solidification of Pb crystals are observed to be related to the crystal habit planes of Pb, and the preferred orientation exhibited in the columnar zone of an ingot of Pb is observed to related to the mode of solidification. In zone-refined lead, the mode of solidification is such as to produce a 〈111〉 preferred orientation. With the addition of 5 × 10 −4 wt. per cent Ag, the mode of solidification changes and a 〈100〉 preferred orientation is produced. On observe que la morphologie des formes de croissance associée aux divers modes de solidification de cristaux de Pb est en relation avec les plans d'habitat cristallins de plomb et que le mode d'orientation préférentielle qui apparaît dans la zone basaltique d'un lingot de plomb est en relation avec le mode de solidification. Dans le plomb raffiné par la méthode de la zone fondue, le mode de solidification est tel qu'il se produit une orientation préférentielle en 〈111〉. Par addition de 5 × 10 −4% en poids d'Ag, le mode de solidification est modifié et une orientation préférentielle en 〈100〉 se produit. Es wurde beobachtet, dass die Morphologie der Wachstumsformen, wie sie bei den verschiedenen Arten der Kristallisation von Blei entstehen, mit den Habitus-Ebenen von Pb in Beziehung stehen, und weiterhin, dass die bevorzugte Richtung in der Zone der Stengelkristallisation eines Blei-Gusstücks mit der Art der Erstarrung zusammenhängt. In zonengereinigtem Blei ist die Erstarrungsart derart, dass sie eine 〈111〉-Vorzugsorientierung hervorruft. Bei Zufügen von 4 × 10 −4 Gew.-Prozent Ag ändert sich die Ersterrungsart, sodass eine 〈100〉-Vorzugsorientierung entsteht.