On the structure and migration of incoherent interphase boundaries between f.c.c. and b.c.c. crystals

• Published in: Acta metallurgica 1974-01, Vol.22 (2), p.141-143
• Main Authors: Bäro, G, Gleiter, H
• Format: Article
• Language: English
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(74)90003-0

Observations by transmission electron microscopy on the migration of interphase boundaries between α-brass (f.c.c.-structure) and β-brass (b.c.c.-structure) are reported. The observations suggest that interphase boundary migration may occur by the movement of steps with a height of about 20–100 A along the plane of the boundary. The mechanism may be understood in terms of the different atomic structure of the steps and the segments of the boundaries between them. Les auteurs présentent des observations de la migration des joints interphases entre le laiton α (structure cfc) et le laiton β (structure cc) effectuées par microscopis électronique en transmission. Les observations suggèrent que la migration du joint interphase peut être produite par le déplacement de marches ayant une hauteur de 20 à 100 Å environ suivant plan du joint. Le mécanisme peut être expliqué par la différence de structure atomique entre les marches et les segments de joint qui les lient. Es wird über elektronenmikroskopische Beobachtungen der Wanderung von Phasengrenzflächen zwischen α-Messing (k.f.z.-Struktur) und β-Messing (k.r.z.-Struktur) borichtet. Die Beobachtungen ergeben, daβ die Wanderung der Phasengrenzfläche durch eine Bewegung von Stufen der Höhe 20 bis 100 Å entlang der Grenzebene erfolgt. Der Mechanismus kann anhand der atomistischen Struktur der Stufen, die sich von der Struktur der der Grenzflüchensegmente zwischen den unterscheidet, Stufen verstanden werden.