On the interaction of cleavage cracks with second phase particles

• Published in: Acta metallurgica 1975-01, Vol.23 (2), p.239-243
• Main Author: Ahlquist, C.Norman
• Format: Article
• Language: English
• ISSN: 0001-6160
• DOI: 10.1016/0001-6160(75)90189-3

The interaction of {100} cleavage cracks with hard and soft second phase particles is described in LiF and MgO single crystals. The principal effect of the second phase particles is to change the cleavage step density. The apparent fracture surface energy, γ i , of MgO is increased by one hundred per cent by the presence of cube shaped 10 μm on a side and spaced at 50 μm. The measured increase in γ i is consistent with the increased work done in forming cleavage steps by shearing at a stress equal to the theoretical shear strength. On décrit l'interaction entre les fissures de clivage {100} et les particules dures et molles d'une seconde phase dans des monocristaux de LiF et de MgO. Le principal effect des particules de la seconde phase est de modifier la densité des matches de clivage. L'énergie superficielle apparente de rupture γ i du MgO est augmentée d'un pour cent par la présence de cavités cubiques de 10 μm de coté espacées de 50 μm. L'augmentation de γ i measurée est compatible avec l'augmentation de travail nécessaire pour former les les marches de clivage par cisaillement sons une contrainte égale à la résistance théorique au cisaillement. Die Wechselwirkung zwischen {100}-Spaltrissen und harten und weichen Teilchen der zweiten Phase wird für LiF- and MgO-Einkristalle beschrieben. Der Haupteinfluβ der Teilchen besteht in einer Änderung der Spaltstufendichte. Durch die Gegenwart kubischer Hohlräume von 10 μm Gröβe und 50 μm Abstand wird die Bruchflächenenergie γ i von MgO um hundert Prozent erhöht. Die gemessene Erhöhung von γ i ist konsistent mit der erhöhten Arbeit bei der Bildung von Spaltstufen durch Scherung bei der theoretischen Scherfestigkeit.