Products formed in an aged concrete

• Published in: Cement and concrete research 1981-01, Vol.11 (3), p.443-454
• Main Authors: Cole, W.F., Lancucki, C.J., Sandy, M.J.
• Format: Article
• Language: English
• ISSN: 0008-8846; 1873-3948
• DOI: 10.1016/0008-8846(81)90116-2

At a dam in Australia the concrete shows a widespread reaction that has caused surface cracking, and possibly a tightening up of gates that control the flow of water through diversion tunnels. The reaction has produced reaction rims to the aggregate, a crystallization of zeolite A-like material within the aggregate and in pores in the concrete, in addition to the precipitation of amorphous alkali-silicate hardened gel in other concrete pores. The hardened gel is sometimes associated with trona and is metastable. It tends to transform into zeolite A-like material or analcite. The reaction products are low in alumina and high in silica. Possible reaction mechanisms are discussed. In einem Damm in Australien zeigt der Beton eine ausgedehnte Reaktion auf, die eine oberflächliche Rissbildung sowie in einigen Fällen eine zu enge Passung der den Wasserdurchfluss der Umläufe steuernden Schleusetoren zur Folge hat. Die Reaktion hat die Entstehung von Reaktionsrändern an den Zuschlägen, ein Auskristallisieren eines Materials, das dem Zeolit-A ähnlich ist, innerhalb des Auschlages und in den Poren des Betons, sowie die Ausfällung in anderen Betonporen eines amorphen, aus Alkalisilikat bestehenden, erstarrten Gels veranlasst. Das erstarrte Gel kommt gelegentlich mit Trona vor, und ist metastabil. Es neigt dazu, sich in einen Zeolit-A ähnelnden Stoff oder in Analzit umzuwandeln. Die Reaktionsprodukte sind tonerdearm und kieselreich. Mögliche Reaktionsmechanismen werden besprochen.