The annealing of a quenched uranium-5 at % molybdenum alloy

• Published in: Journal of nuclear materials 1962-09, Vol.7 (1), p.72-84
• Main Author: May, G.H.
• Format: Article
• Language: English
• ISSN: 0022-3115; 1873-4820
• DOI: 10.1016/0022-3115(62)90195-2

Three reactions have been observed in the annealing of γ-quenched U-5 at % Mo: 1. (1) age-hardening in the supersaturated α b' phase; 2. (2) over-ageing with recrystallisation and discontinuous precipitation of non-equilibrium γ; and 3. (3) a second recrystallisation with re-precipitation to form a pearlitic structure. Mechanisms are proposed for all three reactions, and a possible explanation of the irradiation-swelling properties of the quenched structure is suggested. On a observé 3 réactions au cours du recuit d'un alliage d'uranium à 5 % At Mo trempé depuis la phase γ: 1. 1°) Durcissement structural dans la phase α b' sursaturée. 2. 2°) Survieillissement avec recristallisation et précipitation discontinue de γ hors d'équilibre. 3. 3°) Une seconde recristallisation avec reprécipitation pour former une structure perlitique. Des mécanismes sont proposés pour toutes ces réactions et une explication possible des propriétés de gonflement sous irradiation de la structure trempée est suggérée. Bei der Glühung von abgeschreckten Legierungen aus γUran−5 %-At Mo wurden 3 Reaktionen beobachtet. 1. 1. Alterungshärtung in der übersättigsten α b' Phase. 2. 2. Überalterung mit Rekristallisation und diskontinuierlicher Ausscheidung von nicht im Gleichgewicht befindlichem γ. 3. 3. Sekundäre Rekristallisation mit Wiederausscheidung zur Bildung einer perlitischen Struktur. Es wird ein Mechanismus für alle 3 Reaktionen vorgeschlagen. Eine mögliche Erklärung für die Eigenschaften bei Bestrahlungsschwellung einer abgeschreckten Struktur wird angedeutet.