Surface damage caused by polyvinyl chloride sliding on steel

• Published in: Wear 1959, Vol.2 (3), p.183-194
• Main Author: James, D.I.
• Format: Article
• Language: English
• ISSN: 0043-1648; 1873-2577
• DOI: 10.1016/0043-1648(59)90003-1

A brief survey is given of the different types of debris and surface damage encountered during friction experiments. The most prominent feature is the formation of rolls which lie at right angles to the direction of motion. There appears to be a critical temperature below which rolls do not form. Above this temperature rolls form very freely and frequently the coefficient of friction falls. It is suggested that there may be some connection between rolls and Schallamach abrasion ridges. The formation of other types of debris is also discussed. Es wird eine kurze Übersicht gegeben von den verschiedenen Typen Verschleiss-Trümmern und der Oberflächenbeschädigung, die bei Reibungsexperimenten gefunden wurde. Die am meisten auffallende Erscheinung ist die Bildung von Rollen, die senkrecht zur Bewegungsrichtung liegen. Es besteht scheinbar eine kritische Temperatur unterhalb derer die Rollen nicht entstehen. Überhalb dieser Temperatur bilden sich die Rollen leicht aus, häufig nimmt zugleich der Reibungskoeffizient ab. Zwischen diesen Rollen und Schallamach's Abriebsriffeln besteht vermutlich ein Zusammenhang. Die Bildung anderer Formen von Abriebtrümmern wird ebenfalls besprochen.