Effect of anodic oxide films on the polarization characteristics of Al

• Published in: Corrosion science 1968, Vol.8 (12), p.907-915
• Main Authors: Diggle, J.W., Downie, T.C., Goulding, C.W.
• Format: Article
• Language: English
• ISSN: 0010-938X; 1879-0496
• DOI: 10.1016/S0010-938X(68)80144-1

Cathodic and anodic polarization curves of potential-equilibrated porous anodic oxide films on Al have been determined in Cl − solutions at pH 0–3. For the h.e.r. high Tafel b values, 0·18–0·30 depending upon solution pH, were obtained. A minimum potential was also observed during cathodic polarization. The polarization characteristics did not depend significantly on the initial oxide film preparation method. On a déterminé des courbes de polarisation anodiques et cathodique de pellicules poreuses d'oxyde d'aluminium avec stabilisation de la tension, dans des solutions de Cl − de pH 0 à 3. Pour le (h.e.r.) on a obtenu des hautes valeurs du facteur b de Tafel soit de 0,18 à 0,30 selon le pH de la solution. Les caractéristiques de la polarisation ne dépendent pas de façon significative de la méthode de préparation de la pellicule initiale d'oxyde. Stationäre kathodische und anodische Stromdichte-Potential-Kurven von porösen anodischen Oxidschichten des Aluminiums wurden in chloridhaltigen Lösungen bei einem pH-Wert zwischen 0 und 3 aufgenommen. Die erhaltenen Tafel-Geraden hatten Steigungen, die vom pH-Wert der Lösung abhingen und zwischen b = 0,18 und b = 0,30 lagen. Bei kathodischer Polarisation ergab sich ein Potentialminimum. Der Verlauf der Stromdichte-Potential-Kurven hängt nur wenig vom Herstellungsverfahren der Oxidschichten ab.