Reaction behaviour of Al2O3 and SiO2 in high alumina coal fly ash during alkali hydrothermal process
The reaction behaviours of Al2O3 and SiO2 in high alumina coal fly ash under various alkali hydrothermal conditions were studied. The means of XRD, XRF, FTIR and SEM were used to measure the mineral phase and morphology of the solid samples obtained by different alkali hydrothermal treatments as wel...
Saved in:
Published in: | Transactions of Nonferrous Metals Society of China 2015-06, Vol.25 (6), p.2065-2072 |
---|---|
Main Authors: | , , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The reaction behaviours of Al2O3 and SiO2 in high alumina coal fly ash under various alkali hydrothermal conditions were studied. The means of XRD, XRF, FTIR and SEM were used to measure the mineral phase and morphology of the solid samples obtained by different alkali hydrothermal treatments as well as the leaching ratio of SiO2 to Al2O3 in alkali solution. The results showed that with the increase of the hydrothermal treating temperature from 75 to 160 °C, phillipsite-Na, zeolite A, zeolite P, and hydroxysodalite were produced sequentially while the mullite and corundum phase still remained. Zeolite P was massively formed at low-alkali concentration and the hydroxysodalite was predominantly obtained at high-alkali concentration. By the dissolution of aluminosilicate glass and the formation of zeolites together, the leaching efficiency of SiO2 can reach 42.13% with the mass ratio of Al2O3/SiO2 up to 2.19:1. |
---|---|
ISSN: | 1003-6326 |
DOI: | 10.1016/S1003-6326(15)63816-X |