A novel strengthening strategy for diffusion bonded joint of AlCoCrFeNi2.1 eutectic high entropy alloy to 304 stainless steel

To explore the potential engineering applications of eutectic high entropy alloys (EHEA), the interfacial microstructure and mechanical properties of the diffusion bonded joint between AlCoCrFeNi2.1 EHEA and 304 stainless steel were investigated. The diffusion zone was composed of solid solution zon...

Full description

Saved in:
Bibliographic Details
Published in:Transactions of Nonferrous Metals Society of China 2023-07, Vol.33 (7), p.2121-2135
Main Authors: LI, Peng, SUN, Hao-tian, LI, Chao, WU, Bao-sheng, YANG, Jiang, JIANG, Yu, DONG, Hong-gang
Format: Article
Language:English
Subjects:
304 stainless steel
AlCoCrFeNi2.1 eutectic high entropy alloy
diffusion bonding
shear strength
strengthening mechanism
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:To explore the potential engineering applications of eutectic high entropy alloys (EHEA), the interfacial microstructure and mechanical properties of the diffusion bonded joint between AlCoCrFeNi2.1 EHEA and 304 stainless steel were investigated. The diffusion zone was composed of solid solution zone and Fe2Al5 intermetallic compound zone. Due to the difference in the element diffusion rates between the dissimilar base metals and that between the two phases of EHEA, a solid solution region composed of FCC phase and γ-Fe phase is constructed on the EHEA side near the interface, which enhances the shear strength of joint. Besides, the shear strength of joint first increases and then decreases. The maximum shear strength of 355 MPa is obtained at 980 °C, 60 min, and 30 MPa. The interlocking structure and local solid solution structure are formed in the diffusion zone, thus synergistically enhancing the shear strength of joint.