Effect of Mischmetal on As-cast Microstructure and Mechanical Properties of M2 High Speed Steel

• Published in: Journal of iron and steel research, international international, 2015-03, Vol.22 (3), p.245-249
• Main Authors: LIU, Qiu-xiang, LU, De-ping, LU, Lei, HU, Qiang, FU, Qing-feng, ZHOU, Zhe
• Format: Article
• Language: English
• Subjects: Applied and Technical Physics; as-cast microstructure; Engineering; eutectic carbide; M2 high speed steel; M2高速钢; Machines; Manufacturing; Materials Engineering; Materials Science; Metallic Materials; mischmetal; Physical Chemistry; Processes; 共晶碳化物; 力学性能; 弯曲强度; 扫描电子显微镜; 混合稀土金属; 金属混合物; 铸态组织
• ISSN: 1006-706X; 2210-3988
• DOI: 10.1016/S1006-706X(15)60037-1

High speed steel has been widely used in various fields due to their excellent red hardness and good wear resistance. However, the influence of mischmetal (Ce-La) on the as-cast microstructures and mechanical properties of high speed steel has rarely been reported. Thus, the microstructure and mechanical properties of M2 high speed steel with addition of mischmetal (Ce-La) were investigated. The morphology and distribution of the eutectic carbides of the steel were observed by using optical microscopy and scanning electron microscopy, and the impact toughness and bending strength were tested. The results show that adding mischmetal has an obvious effect on the microstructure and mechanical properties of M2 high speed steel. The coarse eutectic structure is refined, the weak connection of the carbide networks is broken and the flake carbides become short and fine. More networks of eutectic carbides dissolve into the matrix. When a suitable adding content of mischmetal is selected, for example, 0.3 mass%, the impact strength and bending strength can increase by 27% and 10.76% compared with that without mischmetal, respectively.