Layer orientation effects on the R-curve behavior of multilayered alumina–zirconia composites
The crack growth resistance ( R-curve) behavior of multilayered alumina–zirconia composites was measured using a single-edge-V-notched-beam (SEVNB) testing method in which crack initiation and extension were observed via in situ optical microscopy. The influence of the relative layer orientation wit...
Saved in:
Published in: | Composites. Part B, Engineering Engineering, 2006, Vol.37 (6), p.449-458 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | The crack growth resistance (
R-curve) behavior of multilayered alumina–zirconia composites was measured using a single-edge-V-notched-beam (SEVNB) testing method in which crack initiation and extension were observed via in situ optical microscopy. The influence of the relative layer orientation with respect to the crack-tip front through the composite on the resulting
R-curves were measured and was found to have a pronounced influence on the measured crack growth resistance behavior. By increasing the layer offset, the specific influence of a given feature within the layered structure on the measured
R-curve behavior was found to diminish. |
---|---|