Effect of silica fume and colloidal graphite additions on the EMI shielding effectiveness of nickel fiber cement based composites

• Published in: Construction & building materials 2017-09, Vol.150, p.825-832
• Main Authors: Yao, Wei-lin, Xiong, Guoxuan, Yang, Ying, Huang, Hai-qing, Zhou, Yu-fen
• Format: Article
• Language: English
• Subjects: Cement based composites; Colloidal graphite; Electromagnetic shielding; Nickel fiber; Silica fume
• ISSN: 0950-0618; 1879-0526
• DOI: 10.1016/j.conbuildmat.2017.06.019

•A novel EMI SE materials was production by graphite and nickel fiber added in cement.•The best SE of composites was 45dB in 1–1500MHz frequency range.•Graphite doped with in cement based composites the SE was increased about 18.22dB.•Silica fume doped into cement based composites, the SE was increased 8.35dB. Utilization of silica fume and colloidal graphite in nickel fiber cement based composites as a mean of improving the dispersity of nickel fiber and the electromagnetic interference (EMI) shielding effectiveness (SE) of cement based composites. This study aimed of test the EMI SE of cement based composites in 1–1500MHz of the frequency range by coaxial cable method. The conductivity of cement based composites was test by four-point probe meter. The uniformity distribution of nickel fiber, silica fume and colloidal graphite was characterized by scanning electron microscopy. The results obtained indicate the nickel fiber has great effects on the EMI SE of cement based composites. With the content of nickel fiber was increased, the EMI SE of the composites were gradually increasing. When the nickel fiber was doping by 9.0 vol.%, the average SE of cement composites was reached 21.78dB, the maximum SE was 24.48dB in 120MHz. When 20 wt.% of silica fume and 9.0 vol.% of nickel fiber were added in a cement matrix, the shielding property of the composite was best, the average SE was reached 30.13dB, the maximum SE was 35.50dB in 30MHz. The best EMI SE was achieved by the sample comprised of colloidal graphited 20 wt.% and nickel fiber 5.0 vol.%, as exhibiting the average SE was reached 45.0dB, the largest SE was 51.19dB at 1170MHz, indicating a synergistic effect of colloidal graphite and nickel fiber.