Failure study of an aircraft engine high pressure turbine (HPT) first stage blade

•The fracture cause of an aircraft engine high pressure turbine (HPT) first stage blade was determined.•This fracture was produced by a thermo-mechanical fatigue (TMF) mechanism.•The material, René 142 type nickel superalloy, has been completely characterized.•The cracks were originated on the blade...

Full description

Saved in:
Bibliographic Details
Published in:Engineering failure analysis 2023-07, Vol.149, p.107251, Article 107251
Main Authors: García-Martínez, María, del Hoyo Gordillo, Juan Carlos, Valles González, Mª Pilar, Pastor Muro, Ana, González Caballero, Beatriz
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:•The fracture cause of an aircraft engine high pressure turbine (HPT) first stage blade was determined.•This fracture was produced by a thermo-mechanical fatigue (TMF) mechanism.•The material, René 142 type nickel superalloy, has been completely characterized.•The cracks were originated on the blade surface due to pitting corrosion and coating oxidation. In jet engines, almost 50% of failures are located in the damage of turbine blades and discs. This paper presents the study to determine the root cause of the failure of a high-pressure temperature blade in a turbofan engine. Visual observation of the blades indicated that initially-one blade was fractured. Subsequently, detachment of the airfoil from this blade and its impact with the rest of the blades of the first turbine disc trigged a catastrophic damage to them and affected later stages blades. Chemical, microstructural and mechanical characterization determined that blade material corresponded to René 142 nickel superalloy. The observed fractographic characters by optical and scanning electron microscopy showed that the fracture of the first damaged blade was due to a thermo-mechanical fatigue mechanism. The fatigue phenomenon was initiated by corrosion pitting on the root surface of the mentioned blade and progressed due to the cyclic stresses and temperature gradients.