Joining of SiCf/SiC using a layered Ti3SiC2-SiCw and TiC gradient filler

A layered filler consisting of Ti3SiC2-SiC whiskers and TiC transition layer was used to join SiCf/SiC. The effects of SiCw reinforcement in Ti3SiC2 filler were examined after joining at 1400 or 1500 °C in terms of the microstructural evolution, joining strength, and oxidation/chemical resistances....

Full description

Saved in:
Bibliographic Details
Published in:Journal of the European Ceramic Society 2020-04, Vol.40 (4), p.1043-1051
Main Authors: Fitriani, Pipit, Kwon, Heejin, Zhou, Xiaobing, Yoon, Dang-Hyok
Format: Article
Language:English
Subjects:
A. SiCf/SiC
B. Joining
C. Ti3SiC2
D. SiC whisker
E. Mechanical properties
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A layered filler consisting of Ti3SiC2-SiC whiskers and TiC transition layer was used to join SiCf/SiC. The effects of SiCw reinforcement in Ti3SiC2 filler were examined after joining at 1400 or 1500 °C in terms of the microstructural evolution, joining strength, and oxidation/chemical resistances. The TiC transition layer formed by an in-situ reaction of Ti coating resulted in a decrease in thermal expansion mismatch between SiCf/SiC and Ti3SiC2, revealing a sound joint without cracks formation. However, SiCf/SiC joint without TiC layer showed formation of cracks and low joining strength. The incorporation of SiCw in Ti3SiC2 filler showed an increase in joining strength, oxidation, and chemical etching resistance due to the strengthening effect. The Ti3SiC2 filler containing 10 wt.% SiCw along with the formation of TiC was the optimal condition for joining of SiCf/SiC at 1400 °C, showing the highest joining strength of 198 MPa as well as improved oxidation and chemical resistance.
ISSN:0955-2219
1873-619X
DOI:10.1016/j.jeurceramsoc.2019.11.080