Enhancement of order degree and perpendicular magnetic anisotropy of L10 ordered Fe(Pt,Pd) alloy film by introducing a thin MgO cap-layer

• Published in: Journal of magnetism and magnetic materials 2016-07, Vol.410, p.81-88
• Main Authors: Noguchi, Youhei, Ohtake, Mitsuru, Futamoto, Masaaki, Kirino, Fumiyoshi, Inaba, Nobuyuki
• Format: Article
• Language: English
• Subjects: Epitaxial growth; Fe(Pt,Pd) alloy; L10 ordering; Perpendicular magnetic anisotropy; Thin film
• ISSN: 0304-8853
• DOI: 10.1016/j.jmmm.2016.03.011

Fe50PtxPd50−x (at%, x=0–50) alloy films of 10nm thickness with and without 2-nm-thick MgO cap-layers are prepared on MgO(001) single-crystal substrates by employing a two-step method consisting of low-temperature deposition at 200°C followed by high-temperature annealing at 600°C. The influences of MgO cap-layer on the structure and the magnetic properties are investigated. Fe50PtxPd50−x films epitaxially grow on the substrates at 200°C. The Fe50Pd50 and the Fe50Pt12.5Pd37.5 films are respectively composed of (001) single-crystals with disordered fcc-based (A1) and bcc-based (A2) structures. The films with x>25 consist of mixtures of A1 and A2 crystals. The volume ratio of A2 to A1 crystal decreases with increasing the x value from 25 to 50. The in-plane and out-of-plane lattices are respectively expanded and shrunk due to accommodation of lattice mismatch between film and substrate. When the films are annealed at 600°C, phase transformation to L10 ordered phase takes place. L10 phase transformation of Fe50PtxPd50−x film is promoted for a sample with MgO cap-layer and the order degree is higher than that without cap-layer. Furthermore, L10 ordering with the c-axis perpendicular to the substrate surface is enhanced for the film with cap-layer. The cap-layer is considered to be giving a tension stress to the magnetic film in lateral direction which promotes L10 ordering with the c-axis perpendicular to the substrate. Deposition of cap-layer is shown effective in achieving higher order degree and in enhancing perpendicular magnetic anisotropy with Fe(Pt,Pd) films. •MgO-cap-layer effects are studied for Fe(Pt,Pd) films on MgO(001) substrates.•The cap-layer enhances L10-ordering and c-axis aligning to be perpendicular.•The film strain caused by the cap-layer is interpreted to be the major reason.