Influence of manganese on magnetic and electronic properties of ZnCr2Se4

• Published in: Materials research bulletin 2012-08, Vol.47 (8), p.1881-1886
• Main Authors: Jendrzejewska, Izabela, Zajdel, Paweł, Heimann, Jan, Krok-Kowalski, Józef, Mydlarz, Tadeusz, Mrzigod, Janusz
• Format: Article
• Language: English
• Subjects: A. Inorganic compounds; A. Magnetic materials; B. Crystal growth; C. Photoelectron spectroscopy; D. Magnetic properties
• ISSN: 0025-5408; 1873-4227
• DOI: 10.1016/j.materresbull.2012.04.029

[Display omitted] ► The ZnCr2Se4 – single crystals doped with manganese. ► Chemical vapor transport with CrCl3 as transport agent. ► 3d3 electronic configuration of Cr3+ ion with localized magnetic moment of about 3μB. ► Magnetic parameters increase with increasing Mn amount in single crystals. The Zn1−xMnxCr2Se4 crystals were prepared by chemical vapor transport in closed silica tubes using ZnSe and MnSe with CrCl3 as the transport agent. Four crystals with different Mn content (x=0.12, 0.13, 0.18 and 0.24) were studied by X-ray photoelectron spectroscopy (XPS) and magnetic measurements in order to determine influence of manganese on their magnetic and electronic properties. The XPS revealed no change of chemical shifts of Cr core lines indicating a Cr3+ (3d3) electronic configuration. Magnetization measurements revealed a systematic increase in saturation magnetic moments from 6.32μB/mol for x=0.12 to 7.63μB/mol for x=0.24, as well as effective paramagnetic Bohr magneton numbers from 4.87μB/mol for x=0.12 to 6.91μB/mol for x=0.24.