High-entropy perovskite oxide nanofibers as efficient bidirectional electrocatalyst of liquid-solid conversion processes in lithium-sulfur batteries

• Published in: Nano energy 2023-02, Vol.106, p.108037, Article 108037
• Main Authors: Tian, Liyuan, Zhang, Ze, Liu, Sheng, Li, Guoran, Gao, Xueping
• Format: Article
• Language: English
• Subjects: Electrocatalyst; High-entropy oxides; Liquid-solid conversion; Lithium-sulfur batteries; Perovskite nanofibers
• ISSN: 2211-2855
• DOI: 10.1016/j.nanoen.2022.108037

Transition metal oxides are a class of promising host materials of sulfur for lithium-sulfur (Li-S) batteries due to their robust polysulfide adsorption, and catalytic effect on sulfur redox reaction. It is proven that the adsorption-catalysis property can benefit a lot from incorporating multiple metal elements, and high-entropy oxides (HEOs) show good competitive potential for durable Li-S batteries. Herein, HEO nanofibers are designed as bidirectional catalytic host of sulfur to promote both the reduction of soluble intermediates and the re-oxidation of insoluble products. Specifically, the high-entropy perovskite oxide La0.8Sr0.2(Cr0.2Mn0.2Fe0.2Co0.2Ni0.2)O3 (HE-LSMO) nanofibers prepared via an electrospinning-calcination method show a unique porous fibrous structure for incorporation with sulfur. The introduced multiple metal elements can effectively modulate the binding strength of soluble polysulfides, and HE-LSMO nanofibers act as bidirectional electrocatalyst for the liquid-solid conversion processes between soluble polysulfides and insoluble Li2S, which is enabled by the high entropic contribution. As a result, the S/HE-LSMO cathode with a sulfur loading of 8.4 mg cm−2 shows a high areal capacity of 6.6 mAh cm−2 at low electrolyte/sulfur ratio of 5.3 μL mg−1, as well as good cycle stability. This work provides a foundation understanding of the bidirectional catalytic role of HEOs toward practical Li-S batteries. [Display omitted] •Porous La0.8Sr0.2(Cr0.2Mn0.2Fe0.2Co0.2Ni0.2)O3 nanofibers were prepared via an electrospinning-calcination method.•High configuration entropy contributes to the formation of a single perovskite phase.•The multiple metal elements effectively modulate the binding strength of polysulfides.•The oxide acts as a bidirectional catalyst to promote the reduction of polysulfides and the oxidation of Li2S.•High areal capacity of 6.6 mAh cm−2 is realized at a sulfur loading of 8.4 mg cm−2 and an E/S ratio of 5.3 μL mg−1.