Spectroscopic study and visible luminescence of Tb3+ ions in CaF2 crystal co-activated with Yb3

High quality crystals with composition of Ca0.95Tb0.05F2.05 and Ca0.85Tb0.05Yb0.1F2.15 were grown by Bridgman-Stockbarger technique. Yb3+ ions were used as a sensitizer for Tb3+ ions. Optical properties were measured, including the absorption spectrum, emission spectrum, and fluorescence decay curve...

Full description

Saved in:
Bibliographic Details
Published in:Optical materials 2025-01, Vol.158, p.116481, Article 116481
Main Authors: Nekhoroshikh, Anastasiya V., Konyushkin, Vasily A., Zverev, Petr G.
Format: Article
Language:English
Subjects:
Calcium fluoride
Cooperative process
Judd-ofelt theory
Luminescence
Terbium ions
Visible laser
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:High quality crystals with composition of Ca0.95Tb0.05F2.05 and Ca0.85Tb0.05Yb0.1F2.15 were grown by Bridgman-Stockbarger technique. Yb3+ ions were used as a sensitizer for Tb3+ ions. Optical properties were measured, including the absorption spectrum, emission spectrum, and fluorescence decay curves. Judd-Ofelt theory was used to analyze the spectroscopic parameters. Fluorescence branch ratio, transition probability, radiative and fluorescence lifetimes, and quantum efficiency were determined. The emission cross section of Tb3+ ions in Tb:CaF2 and Tb/Yb:CaF2 crystals for the green emission at 544 nm, corresponding to the transitions of 5D4→7F5 were calculated to be 4.61 × 10−22 cm2 and 4.60 × 10−22 cm2, respectively. Our experiments have shown that doping with Yb3+ ions does not significantly affect the spectral properties of Tb3+ ions in CaF2 crystal. Quadratic dependence of the emission intensity of Tb3+ ion in Tb/Yb:CaF2 crystal on the intensity of a diode laser at 955 nm proved that the excitation of Tb3+ ion occurs due to the cooperative process of transferring the excitation from two Yb3+ ions to one neighboring Tb3+ ion. The Tb/Yb:CaF2 crystal can be considered as a promising up-converting medium for creating diode-pumped visible phosphorus and active laser media. •Spectral properties of Tb3+ ions are not affected by Yb3+ in Ca0.85Tb0.05Yb0.1F2.15 crystal.•Ga–As diode laser effectively excites Tb3+ ions in Tb/Yb:CaF2 crystal due to cooperative up-conversion process•Tb/Yb:CaF2 crystal is promising for creating diode-pumped visible phosphorus and active laser media.
ISSN:0925-3467
DOI:10.1016/j.optmat.2024.116481