Rapid crystallization of poly(l-lactic acid) induced by a nanoscaled zinc citrate complex as nucleating agent

A nanoscaled zinc citrate complex (ZnCC) was synthesized by the reaction of zinc acetate and citric acid using solution method. As a new eco-friendly nucleating agent, ZnCC was introduced into poly(l-lactic acid) (PLLA) via melt blending. The nonisothermal and isothermal crystallization, melting beh...

Full description

Saved in:
Bibliographic Details
Published in:Polymer (Guilford) 2012-08, Vol.53 (19), p.4300-4309
Main Authors: Song, Ping, Chen, Guangyi, Wei, Zhiyong, Chang, Ying, Zhang, Wanxi, Liang, Jicai
Format: Article
Language:English
Subjects:
annealing
Applied sciences
citrates
citric acid
cooling
Crystallization
Exact sciences and technology
mechanical properties
Nucleating agent
Organic polymers
Physicochemistry of polymers
Poly(l-lactic acid)
polymers
Properties and characterization
storage modulus
talc
temperature
thermal properties
zinc
zinc acetate
Zinc citrate complex
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:A nanoscaled zinc citrate complex (ZnCC) was synthesized by the reaction of zinc acetate and citric acid using solution method. As a new eco-friendly nucleating agent, ZnCC was introduced into poly(l-lactic acid) (PLLA) via melt blending. The nonisothermal and isothermal crystallization, melting behavior, crystalline morphology and mechanical properties of the PLLA/ZnCC blends were investigated. It is found that ZnCC exhibits much more prominent nucleation activity on the crystallization of PLLA than conventional nucleating agent talc and commercial zinc citrate (ZnCit). By loading 0.05 wt% ZnCC, PLLA can complete crystallization upon cooling at 10 °C/min, and the crystallization peak shifts to a higher temperature with increasing ZnCC content. In the case of isothermal crystallization from the melt, the addition of ZnCC leads to a shorter crystallization time and a faster overall crystallization rate. Besides, the nucleation density of PLLA increases and the spherulite size decreases significantly in the presence of ZnCC. Epitaxy is the possible mechanism to elucidate the nucleation phenomenon of PLLA/ZnCC system. The tensile results show that ZnCC has a plasticization effect on the amorphous PLLA. Through a short-time annealing procedure, the mechanical properties such as tensile modulus and storage modulus of PLLA are improved by the addition of ZnCC. [Display omitted]
ISSN:0032-3861
1873-2291
DOI:10.1016/j.polymer.2012.07.032