Effect of drawing stress on mesophase structure formation of poly(ethylene 2,6-naphthalene dicarboxylate) fiber just after the neck-drawing point

• Published in: Polymer (Guilford) 2012-08, Vol.53 (19), p.4272-4279
• Main Authors: Kim, Kyoung-Hou, Aida, Ryo, Kang, Young-Ah, Ikaga, Toshifumi, Ohkoshi, Yutaka, Wataoka, Isao, Urakawa, Hiroshi
• Format: Article
• Language: English
• Subjects: Applied sciences; CO2 laser-heated drawing; crystal structure; crystallization; ethylene; Exact sciences and technology; Fibers and threads; Forms of application and semi-finished materials; heat; irradiation; Mesophase structure; Poly(ethylene 2,6-naphthalene dicarboxylate); Polymer industry, paints, wood; polymers; spatial distribution; Technology of polymers; temperature; X-ray diffraction
• ISSN: 0032-3861; 1873-2291
• DOI: 10.1016/j.polymer.2012.07.043

The structural development of poly(ethylene 2,6-naphthalene dicarboxylate) (PEN) fibers was analyzed by in situ X-ray diffraction and fiber temperature measurements. The PEN fiber was drawn continuously under three drawing stresses, where the neck-drawing point was fixed accurately by CO2 laser irradiation heating. The developed crystal structures of the drawn fibers depended on the drawing stresses, that is, only the α-crystal was obtained under a drawing stress of 148 MPa, an α-rich mixed crystal was obtained for 54 MPa, and a β-rich mixed crystal was obtained under 23 MPa stress. Fiber containing over 70% β-crystal was obtained in the third case. Orientation-induced crystallization rates (K) and crystallization induction times (t0) were estimated for the three drawing stresses: K = 2210 s−1 and t0 = 0.5 ms for 148 MPa, K = 940 s−1 and t0 = 1.0 ms for 54 MPa, and K = 655 s−1 and t0 = 4.0 ms for 23 MPa. In addition, the drawing stress acted as a definitive influence not only on the resulting crystal form but also on the chain conformation of the mesophase structure. The d-spacing of the (001′) diffraction increased with drawing stress, and the longer (001′) spacing generated the α-crystal while the comparatively shorter (001′) spacing yielded the β-crystal. The d-spacings of 1.27 and 1.23 nm for the drawing stresses of 148 and 23 MPa, respectively, were somewhat shorter than the c-axis lengths of the α- and β-crystals of 1.32 and 1.27 nm, respectively. [Display omitted]