Effect of initial composition on boron carbide production by SHS process followed by acid leaching
In this study, iron-free boron carbide powders (B4C) were produced from the milled SHS (self-propagating high temperature synthesis) products followed by leaching in an aqueous hydrochloric acid (HCl) media. The SHS mixtures were composed of boron oxide (B2O3), carbon black and magnesium. Thermochem...
Saved in:
Published in: | Solid state sciences 2012-11, Vol.14 (11-12), p.1688-1691 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Subjects: | |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | In this study, iron-free boron carbide powders (B4C) were produced from the milled SHS (self-propagating high temperature synthesis) products followed by leaching in an aqueous hydrochloric acid (HCl) media. The SHS mixtures were composed of boron oxide (B2O3), carbon black and magnesium. Thermochemical simulations were performed to estimate the effect of initial composition on the SHS process. In the SHS experiments, it was found that the formations of boron carbide and magnesium borates were directly related with B2O3 and carbon black contents in the initial SHS mixture. The aqueous HCl leaching of the SHS products did not only eliminate the unwanted byproducts (i.e. MgO, Mg3B2O6 and Mg2B2O5) but also enhanced substantially the pore structure of the particles. Even though the leached SHS particles (d0.5 = 7.96 μm) were much coarser than that of the commercial powder (d0.5 = 1.73 μm), the surface area of the leached product (15.56 m2/g) was found to be larger than that of commercial one (4.92 m2/g).
[Display omitted] |
---|---|
ISSN: | 1293-2558 1873-3085 |
DOI: | 10.1016/j.solidstatesciences.2012.07.004 |