Surface free energy characterization and adhesion performance of mild steel treated based on zirconium conversion coating: A comparative study

The influence of zirconium based conversion coating on the surface free energy and adhesion performance of an epoxy coated mild steel substrate was evaluated before and after post heating. Surface free energy components (γLW, γ+ and γ) of the mild steel were measured before and after surface treatme...

Full description

Saved in:
Bibliographic Details
Published in:Surface & coatings technology 2014-05, Vol.246, p.26-33
Main Authors: Ghanbari, A., Attar, M.M.
Format: Article
Language:English
Subjects:
Adhesion
Applied sciences
Conversion coating
Cross-disciplinary physics: materials science
rheology
Exact sciences and technology
FE-SEM
Materials science
Metals. Metallurgy
Physics
Production techniques
Surface
Surface treatment
Surface treatments
Zirconium
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The influence of zirconium based conversion coating on the surface free energy and adhesion performance of an epoxy coated mild steel substrate was evaluated before and after post heating. Surface free energy components (γLW, γ+ and γ) of the mild steel were measured before and after surface treatment using van Oss–Good method. The obtained data revealed that after formation of the conversion layer, γ−component of the surface increased leading to increment of work of adhesion. This may be attributed to the formation of zirconium compounds and adsorbed fluoride ion on the steel surface, which are evident in the Field Emission Scanning Electron Microscopy (FE-SEM) and Energy Dispersive X-ray spectroscopy (EDX) results, respectively. Pull-off adhesion test was performed for variety of the surface treatments including zirconium conversion coating (ZCC) and traditional phosphate and chromate layers. The results indicate that ZCC increased adhesion strength of mild steel to the organic coating and the zirconium treated mild steel adhesion performance is better than that of the three-cationic phosphate layer. •Surface free energy characterization of zirconium-based conversion coating (ZCC)•Explanation of the surface analysis results employing FE-SEM and EDX technique•Studying the practical adhesion performance of an epoxy coating to Zr treated mild steel using pull-off test•Make a correlation between fundamental and practical adhesion analysis