Syntheses and Properties of Soluble Biphenyl-Based Polyimides from Asymmetric Bis(chlorophthalimide)s

• Published in: Macromolecules 2004-04, Vol.37 (8), p.2754-2761
• Main Authors: Gao, Changlu, Wu, Xuee, Lv, Guanghua, Ding, Mengxian, Gao, Lianxun
• Format: Article
• Language: English
• Subjects: Applied sciences; Exact sciences and technology; Organic polymers; Physicochemistry of polymers; Polymers with particular properties; Preparation, kinetics, thermodynamics, mechanism and catalysts
• ISSN: 0024-9297; 1520-5835
• DOI: 10.1021/ma0350720

A novel synthesis of asymmetric bis(chlorophthalimide)s (3,4-BCPIs) has been established. The polymerizations of them produced higher molecular weight (0.38−0.51 dL/g) polyimides containing biphenyl units than those of isomeric polymers derived from symmetric bis(chlorophthalimide)s (4,4‘-BCPIs) and 3,3‘-BCPIs. The distribution of the formed biphenyl units of head to tail, head to head, and tail to tail in the chain of the polymers was about 58.0:21.0:21.0, determined by 13C NMR spectra of the polymers. The composition of model compounds, determined by HPLC, was well consistent with the 13C NMR spectrum result. Comparing with polymers derived from 4,4‘-BCPIs and 3,3‘-BCPIs, the polymers derived from 3,4-BCPIs showed better solubilities in N,N-dimethylacetamide (DMAc), N,N-dimethylformamide (DMF), and N-methylpyrrolinone (NMP). Flexible films could be cast from the polymer solution with the inherent viscosities of above 0.35 dL/g. The polymer derived from asymmetric bis(chlorophthimide)s gave the highest T g among the isomeric polymers. The 10% weight loss of these polyimides was above 549 °C.