Effect of metal-ligand ratio on the CO 2 adsorption properties of Cu-BTC metal-organic frameworks
Initially, in the synthesis of Cu-BTC MOFs some fraction of Cu was expected to be replaced with Mg to enhance its CO adsorption properties. Indeed, an enhancement in the specific surface area, microporosity and CO adsorption capacity was observed; however, Mg was not detected. Therefore, additional...
Saved in:
Published in: | RSC advances 2018-10, Vol.8 (62), p.35551-35556 |
---|---|
Main Authors: | , , , |
Format: | Article |
Language: | English |
Citations: | Items that this one cites Items that cite this one |
Online Access: | Get full text |
Tags: |
Add Tag
No Tags, Be the first to tag this record!
|
Summary: | Initially, in the synthesis of Cu-BTC MOFs some fraction of Cu was expected to be replaced with Mg to enhance its CO
adsorption properties. Indeed, an enhancement in the specific surface area, microporosity and CO
adsorption capacity was observed; however, Mg was not detected. Therefore, additional syntheses of Cu-BTC MOFs with the same Cu to BTC ratios were performed but in the absence of Mg to explain the observed enhancement. It was found that the adjustment of the Cu-BTC ratio to 1.09 : 1.0, which differs from that reported in the literature, resulted in a Cu-BTC MOF with higher specific BET surface area, larger micropore volume, and consequently, superior CO
adsorption of 9.33 mmol g
at 0 °C and 1 bar. |
---|---|