Effect of a MgO interlayer on the structural and magnetic properties of Co2Cr0.6Fe0.4Al thin films epitaxially grown on GaAs substrates

The effect of a MgO interlayer on the structural and magnetic properties of Co2Cr0.6Fe0.4Al (CCFA) thin films epitaxially grown on GaAs substrates by sputtering was investigated. When the MgO interlayer thickness was 1.0nm or less, the CCFA films were grown with a cube-on-cube relation to GaAs and n...

Full description

Saved in:
Bibliographic Details
Published in:Journal of applied physics 2007-03, Vol.101 (6)
Main Authors: Yano, T., Uemura, T., Matsuda, K.-i., Yamamoto, M.
Format: Article
Language:English
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The effect of a MgO interlayer on the structural and magnetic properties of Co2Cr0.6Fe0.4Al (CCFA) thin films epitaxially grown on GaAs substrates by sputtering was investigated. When the MgO interlayer thickness was 1.0nm or less, the CCFA films were grown with a cube-on-cube relation to GaAs and no significant decrease in either the x-ray diffraction intensity or saturation magnetization was observed. In contrast, when the MgO thickness was 1.5nm or more, the CCFA film was rotated by 45° in the (001) plane with respect to GaAs, and both the x-ray diffraction intensity and saturation magnetization decreased. All samples showed strong magnetic anisotropy, in which a uniaxial anisotropy with an easy axis of [110]GaAs or [1−10]GaAs dominated with a slight cubic anisotropy having an easy axis of ⟨110⟩CCFA superimposed.
ISSN:0021-8979
1089-7550
DOI:10.1063/1.2712164