Fouling communities and degradation of archeological metals in the coastal sea of the Southwestern Gulf of Mexico

Corrosion and biofouling phenomena of cast iron and brass were evaluated under natural conditions to determine the degradation process of archeological artifacts. Field exposure studies of experimental materials were conducted over 15 months at an offshore position in the sea of Campeche in the Gulf...

Full description

Saved in:
Bibliographic Details
Published in:Biofouling (Chur, Switzerland) Switzerland), 2015-01, Vol.31 (5), p.405-416
Main Authors: López Garrido, Pedro H., González-Sánchez, J., Escobar Briones, Elva
Format: Article
Language:English
Subjects:
anodic and cathodic reactions
Archaeology - methods
Biofouling
biological colonization
Corrosion
Gulf of Mexico
metal dissolution
metallic artifacts
Metals - chemistry
Mexico
shipwreck
species richness
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Corrosion and biofouling phenomena of cast iron and brass were evaluated under natural conditions to determine the degradation process of archeological artifacts. Field exposure studies of experimental materials were conducted over 15 months at an offshore position in the sea of Campeche in the Gulf of Mexico. Corrosion was determined by gravimetric measurements. The community structure of the benthic assemblage inhabiting the surfaces of both materials was evaluated. A total of 53 species was identified. The community in both cases was composed of a small number of species. Encrusting, attached and erect life forms were dominant on iron. Attached life forms were dominant on brass. Biofouling produced a decrease in the weight loss measurements of cast iron samples. Biofouling provided a beneficial factor for in situ preservation of iron archeological artifacts in wreck sites.
ISSN:0892-7014
1029-2454
DOI:10.1080/08927014.2015.1048433