Investigation of cracking mechanisms in rubber-modified asphalt through fracture testing of mastic specimens

Rubber modification of asphalt leads to improvement in certain asphalt mixture properties in lab studies, and extension of service life has been reported in a number of field studies. However, modern laboratory cracking tests often produce conflicting results in terms of the expected cracking perfor...

Full description

Saved in:
Bibliographic Details
Published in:Road materials and pavement design 2022-07, Vol.23 (7), p.1544-1563
Main Authors: Rath, Punyaslok, Gettu, Nandita, Chen, Shishi, Buttlar, William G.
Format: Article
Language:English
Subjects:
Asphalt mixes
crack pinning
Cracking (fracturing)
cracking tests
Ductile-brittle transition
Fracture mechanics
Fracture testing
ground tire rubber
modified asphalt
Polymers
Rubber asphalt
Rubber modified asphalt
Service life
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Rubber modification of asphalt leads to improvement in certain asphalt mixture properties in lab studies, and extension of service life has been reported in a number of field studies. However, modern laboratory cracking tests often produce conflicting results in terms of the expected cracking performance of rubber-modified asphalt mixtures. To better understand cracking/toughening mechanisms in rubber modified asphalt materials, a fracture mechanics based test was devised for various unmodified and modified binder systems (unmodified control, polymer- and rubber-modified at various treatment levels). The results of this testing showed that unmodified and polymer-modified specimens failed in a brittle fashion, while the rubber-modified specimens displayed increasing ductile-type failures as the rubber modification level increased. Analysis of the fractured faces of the specimens under a Scanning Electron Microscope also revealed the presence of characteristic tails and cavities in the rubber-modified specimens associated with a crack-pinning-type toughening mechanism.
ISSN:1468-0629
2164-7402
DOI:10.1080/14680629.2021.1905696