Influence of Silicon Morphology and Mechanical Properties of Piston Alloys

In this paper, the influence of silicon particle morphology on mechanical properties of two piston alloys has been reported. Alloys having nominal composition Al-12%Si-1%Ni-0.8%Cu-0.6%Mg (LM13) and Al-17%Si-1%Ni-0.8%Cu-0.6%Mg (LM28) were prepared by melting and casting. The morphology of silicon cry...

Full description

Saved in:
Bibliographic Details
Published in:Materials and manufacturing processes 2005-09, Vol.20 (5), p.777-791
Main Authors: Dwivedi, Dheerendra Kumar, Sharma, A., Rajan, T. V.
Format: Article
Language:English
Subjects:
Artificial age hardening
Cast Al-Si alloys
Eutectic and hypereutectic alloys
Grain refinement
LM13 and LM28
Mechanical properties
Microstructure
Mode of fracture
Modification
Spheroidization
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:In this paper, the influence of silicon particle morphology on mechanical properties of two piston alloys has been reported. Alloys having nominal composition Al-12%Si-1%Ni-0.8%Cu-0.6%Mg (LM13) and Al-17%Si-1%Ni-0.8%Cu-0.6%Mg (LM28) were prepared by melting and casting. The morphology of silicon crystals was changed using additives during the melt treatment and subsequently by heat treatment. Mechanical properties such as hardness, ductility, and tensile strength of experimental alloys were tested. Test results showed that the melt treatment and heat treatment of both the alloys increased the tensile strength, hardness, and ductility. However, the influence of melt treatment on mechanical properties was not as significant as that of heat treatment. Tensile strength and ductility of LM13 was found to be higher than the LM28 alloy under similar conditions. Hardness of LM28 was higher than the LM13 alloy. Optical and SEM studies showed a change in eutectic silicon morphology on melt treatment of LM13. However, change in morphology of primary silicon particles was not significant as for LM28. Heat treatment of both alloys caused spheroidization and better distribution of eutectic silicon crystals. Sharp-edged primary silicon particles were rounded off after the heat treatment of LM28. Scanning electron microscopy (SEM) of tensile fractured surfaces was carried out to study the influence of microstructure on fracture mode. Heat treatment of both alloys promotes dimple fracture. However, as-cast and melt-treated alloys show predominantly cleavage fracture.
ISSN:1042-6914
1532-2475
DOI:10.1081/AMP-200055138