Optical properties of Pb 0.52 Zr 0.48 TiO 3 nanorod arrays: second harmonic generation and multiphoton carrier dynamics

Nonlinear optical properties of poled and unpoled, lead zirconate-titanate (Pb 0.52 Zr 0.48 TiO 3 ) nanorod arrays, grown on Pt-coated Si with ∼200 nm diameter and ∼600 nm height, were investigated. Clear signatures of second harmonic generations (SHG), from 490–525 nm (2.38–2.53 eV) at room tempera...

Full description

Saved in:
Bibliographic Details
Published in:JPhys photonics 2021-07, Vol.3 (3), p.34012
Main Authors: Mudiyanselage, Rathsara R H H, Burton, John, Magill, Brenden A, McMillan, Kiara, Gagliano, Gabriella, Morral, Ada J, Gyu Kang, Min, Kang, Han Byul, Priya, Shashank, Stanton, Christopher J, Khodaparast, Giti A
Format: Article
Language:English
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Nonlinear optical properties of poled and unpoled, lead zirconate-titanate (Pb 0.52 Zr 0.48 TiO 3 ) nanorod arrays, grown on Pt-coated Si with ∼200 nm diameter and ∼600 nm height, were investigated. Clear signatures of second harmonic generations (SHG), from 490–525 nm (2.38–2.53 eV) at room temperature, were observed. Furthermore, time resolved differential reflectivity measurements were performed to study dynamical properties of photoexcited carriers in the range of 690–1000 nm where multiphoton processes were responsible for the photo-excitations. We compared this excitation scheme, which is sensitive mainly to the surface states, to when the photoexcited energy (∼3.1 eV) was close to the band gap of the nanorods. Our results offer promises for employing these nanostructures in nonlinear photonic applications.
ISSN:2515-7647
2515-7647
DOI:10.1088/2515-7647/ac023a