Direct Observation of the Stretching of the Photoinduced Current Relaxation in α-Ga 2 O 3 Schottky Diodes

Relaxation of photoinduced current in α -Ga 2 O 3 -based Schottky diodes was measured. Such Schottky diodes were fabricated using α -Ga 2 O 3 films grown by Halide Vapor Phase Epitaxy (HVPE) on basal plane sapphire. Their photosensitivity in UV-C region was very high and several orders of magnitude...

Full description

Saved in:
Bibliographic Details
Published in:ECS journal of solid state science and technology 2023-12, Vol.12 (12), p.125004
Main Authors: Schemerov, Ivan V., Polyakov, Alexander Y., Vasilev, Anton A., Nikolaev, Vladimir I., Pechnikov, Alexey I., Chernykh, Alexey V., Romanov, Andrey A., Pearton, Stephen J.
Format: Article
Language:English
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:Relaxation of photoinduced current in α -Ga 2 O 3 -based Schottky diodes was measured. Such Schottky diodes were fabricated using α -Ga 2 O 3 films grown by Halide Vapor Phase Epitaxy (HVPE) on basal plane sapphire. Their photosensitivity in UV-C region was very high and several orders of magnitude higher than for visible light. The photoinduced current rise and decay times are found to be quite long, which is attributed to the hole capture by deep acceptors and to the effects of potential fluctuations. Due to these problems the photoinduced current relaxation process consists of several steps and takes more than hundreds of seconds. The characteristic relaxation times were calculated using the logarithmic differential analysis that demonstrated that the build-up and decay processes can be accurately described by stretched exponents with different broadening factors β . It was shown that additional illumination by long-wave light can help to observe the slowing of the relaxation speed. The temperature activation energies for photoinduced current decay and rise times are 0.37 ± 0.03 eV and 0.06 ± 0.005 eV respectively.
ISSN:2162-8769
2162-8777
DOI:10.1149/2162-8777/ad145f