Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes

Pit initiation and repassivation of stainless steels (SS) SS430 and SS304 were investigated under a thin solution film of MgCl2. The potential difference between the SS plate and the thin silver wire set 100 μm above the SS surface was measured during the wet-dry cycles. The wet-dry cycles were carr...

Full description

Saved in:
Bibliographic Details
Published in:Journal of the Electrochemical Society 2015-01, Vol.162 (9), p.C419-C425
Main Authors: Van Nam, Tran, Tada, Eiji, Nishikata, Atsushi
Format: Article
Language:English
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
cited_by cdi_FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683
cites cdi_FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683
container_end_page C425
container_issue 9
container_start_page C419
container_title Journal of the Electrochemical Society
container_volume 162
creator Van Nam, Tran
Tada, Eiji
Nishikata, Atsushi
description Pit initiation and repassivation of stainless steels (SS) SS430 and SS304 were investigated under a thin solution film of MgCl2. The potential difference between the SS plate and the thin silver wire set 100 μm above the SS surface was measured during the wet-dry cycles. The wet-dry cycles were carried out by changing the relative humidity (RH) between 95% and 45% at a constant rate of 5%/h. A rapid potential drop due to initiation of a growth-type pit was observed when the RH was decreased from 95%, while a rapid potential rise owing to repassivation was observed when the RH was increased from 45%. The RHpit and RHrep at the onset of pitting corrosion and repassivation were determined at various temperatures. At 298 K, the RHpit was obtained to be 68%-48% for SS430 and 58%-47% for SS304. The RHrep ranged from 67% to 73% for SS430 and 56%-70% for SS304. The RHpit and RHrep increased significantly as the temperature was increased from 283 K to 313 K.
doi_str_mv 10.1149/2.0151509jes
format article
fullrecord <record><control><sourceid>iop_cross</sourceid><recordid>TN_cdi_crossref_primary_10_1149_2_0151509jes</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>0151509JES</sourcerecordid><originalsourceid>FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683</originalsourceid><addsrcrecordid>eNptkEtPwzAQhC0EEqVw4wf4yIEUb20n8RFFpa1UCcTjHLbJGlylSRS7Ff33GBWJC6d96JvRaBi7BjEBUOZuOhGgQQuzIX_CRmCUTjIAOGUjIUAmKtVwzi6838QTcpWN2PuTC3zZuuAwuK7l2Nb8mXr03u2Pn87yl4Cubcj7uBE1ns---s5TzUPHi0PVuCpqmojviS92W1e7cODFJ7Yf5C_ZmcXG09XvHLO3h9lrsUhWj_Nlcb9KKpnlITFW2qkgJSRKbdeqJoUSsxRMnVMd01baoEEiK0lXKWRg0hzXilCnKktzOWa3R99q6LwfyJb94LY4HEoQ5U875bT8ayfiN0fcdX256XZDG8P9j34DgqFmAQ</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype></control><display><type>article</type><title>Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes</title><source>Institute of Physics:Jisc Collections:IOP Publishing Read and Publish 2024-2025 (Reading List)</source><creator>Van Nam, Tran ; Tada, Eiji ; Nishikata, Atsushi</creator><creatorcontrib>Van Nam, Tran ; Tada, Eiji ; Nishikata, Atsushi</creatorcontrib><description>Pit initiation and repassivation of stainless steels (SS) SS430 and SS304 were investigated under a thin solution film of MgCl2. The potential difference between the SS plate and the thin silver wire set 100 μm above the SS surface was measured during the wet-dry cycles. The wet-dry cycles were carried out by changing the relative humidity (RH) between 95% and 45% at a constant rate of 5%/h. A rapid potential drop due to initiation of a growth-type pit was observed when the RH was decreased from 95%, while a rapid potential rise owing to repassivation was observed when the RH was increased from 45%. The RHpit and RHrep at the onset of pitting corrosion and repassivation were determined at various temperatures. At 298 K, the RHpit was obtained to be 68%-48% for SS430 and 58%-47% for SS304. The RHrep ranged from 67% to 73% for SS430 and 56%-70% for SS304. The RHpit and RHrep increased significantly as the temperature was increased from 283 K to 313 K.</description><identifier>ISSN: 0013-4651</identifier><identifier>EISSN: 1945-7111</identifier><identifier>DOI: 10.1149/2.0151509jes</identifier><language>eng</language><publisher>The Electrochemical Society</publisher><ispartof>Journal of the Electrochemical Society, 2015-01, Vol.162 (9), p.C419-C425</ispartof><rights>2015 The Electrochemical Society</rights><lds50>peer_reviewed</lds50><woscitedreferencessubscribed>false</woscitedreferencessubscribed><citedby>FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683</citedby><cites>FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><link.rule.ids>314,780,784,27924,27925</link.rule.ids></links><search><creatorcontrib>Van Nam, Tran</creatorcontrib><creatorcontrib>Tada, Eiji</creatorcontrib><creatorcontrib>Nishikata, Atsushi</creatorcontrib><title>Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes</title><title>Journal of the Electrochemical Society</title><addtitle>J. Electrochem. Soc</addtitle><description>Pit initiation and repassivation of stainless steels (SS) SS430 and SS304 were investigated under a thin solution film of MgCl2. The potential difference between the SS plate and the thin silver wire set 100 μm above the SS surface was measured during the wet-dry cycles. The wet-dry cycles were carried out by changing the relative humidity (RH) between 95% and 45% at a constant rate of 5%/h. A rapid potential drop due to initiation of a growth-type pit was observed when the RH was decreased from 95%, while a rapid potential rise owing to repassivation was observed when the RH was increased from 45%. The RHpit and RHrep at the onset of pitting corrosion and repassivation were determined at various temperatures. At 298 K, the RHpit was obtained to be 68%-48% for SS430 and 58%-47% for SS304. The RHrep ranged from 67% to 73% for SS430 and 56%-70% for SS304. The RHpit and RHrep increased significantly as the temperature was increased from 283 K to 313 K.</description><issn>0013-4651</issn><issn>1945-7111</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2015</creationdate><recordtype>article</recordtype><recordid>eNptkEtPwzAQhC0EEqVw4wf4yIEUb20n8RFFpa1UCcTjHLbJGlylSRS7Ff33GBWJC6d96JvRaBi7BjEBUOZuOhGgQQuzIX_CRmCUTjIAOGUjIUAmKtVwzi6838QTcpWN2PuTC3zZuuAwuK7l2Nb8mXr03u2Pn87yl4Cubcj7uBE1ns---s5TzUPHi0PVuCpqmojviS92W1e7cODFJ7Yf5C_ZmcXG09XvHLO3h9lrsUhWj_Nlcb9KKpnlITFW2qkgJSRKbdeqJoUSsxRMnVMd01baoEEiK0lXKWRg0hzXilCnKktzOWa3R99q6LwfyJb94LY4HEoQ5U875bT8ayfiN0fcdX256XZDG8P9j34DgqFmAQ</recordid><startdate>20150101</startdate><enddate>20150101</enddate><creator>Van Nam, Tran</creator><creator>Tada, Eiji</creator><creator>Nishikata, Atsushi</creator><general>The Electrochemical Society</general><scope>AAYXX</scope><scope>CITATION</scope></search><sort><creationdate>20150101</creationdate><title>Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes</title><author>Van Nam, Tran ; Tada, Eiji ; Nishikata, Atsushi</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>2015</creationdate><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Van Nam, Tran</creatorcontrib><creatorcontrib>Tada, Eiji</creatorcontrib><creatorcontrib>Nishikata, Atsushi</creatorcontrib><collection>CrossRef</collection><jtitle>Journal of the Electrochemical Society</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Van Nam, Tran</au><au>Tada, Eiji</au><au>Nishikata, Atsushi</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes</atitle><jtitle>Journal of the Electrochemical Society</jtitle><addtitle>J. Electrochem. Soc</addtitle><date>2015-01-01</date><risdate>2015</risdate><volume>162</volume><issue>9</issue><spage>C419</spage><epage>C425</epage><pages>C419-C425</pages><issn>0013-4651</issn><eissn>1945-7111</eissn><abstract>Pit initiation and repassivation of stainless steels (SS) SS430 and SS304 were investigated under a thin solution film of MgCl2. The potential difference between the SS plate and the thin silver wire set 100 μm above the SS surface was measured during the wet-dry cycles. The wet-dry cycles were carried out by changing the relative humidity (RH) between 95% and 45% at a constant rate of 5%/h. A rapid potential drop due to initiation of a growth-type pit was observed when the RH was decreased from 95%, while a rapid potential rise owing to repassivation was observed when the RH was increased from 45%. The RHpit and RHrep at the onset of pitting corrosion and repassivation were determined at various temperatures. At 298 K, the RHpit was obtained to be 68%-48% for SS430 and 58%-47% for SS304. The RHrep ranged from 67% to 73% for SS430 and 56%-70% for SS304. The RHpit and RHrep increased significantly as the temperature was increased from 283 K to 313 K.</abstract><pub>The Electrochemical Society</pub><doi>10.1149/2.0151509jes</doi><tpages>7</tpages></addata></record>
fulltext fulltext
identifier ISSN: 0013-4651
ispartof Journal of the Electrochemical Society, 2015-01, Vol.162 (9), p.C419-C425
issn 0013-4651
1945-7111
language eng
recordid cdi_crossref_primary_10_1149_2_0151509jes
source Institute of Physics:Jisc Collections:IOP Publishing Read and Publish 2024-2025 (Reading List)
title Pit Initiation and Repassivation of Stainless Steels Exposed to Cyclic Relative Humidity Changes
url http://sfxeu10.hosted.exlibrisgroup.com/loughborough?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-01-01T20%3A20%3A01IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-iop_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Pit%20Initiation%20and%20Repassivation%20of%20Stainless%20Steels%20Exposed%20to%20Cyclic%20Relative%20Humidity%20Changes&rft.jtitle=Journal%20of%20the%20Electrochemical%20Society&rft.au=Van%20Nam,%20Tran&rft.date=2015-01-01&rft.volume=162&rft.issue=9&rft.spage=C419&rft.epage=C425&rft.pages=C419-C425&rft.issn=0013-4651&rft.eissn=1945-7111&rft_id=info:doi/10.1149/2.0151509jes&rft_dat=%3Ciop_cross%3E0151509JES%3C/iop_cross%3E%3Cgrp_id%3Ecdi_FETCH-LOGICAL-c378t-9f3f20e403a35fb4de4a3a7619d8ed011c59a9aeef3e5c6171968ab4ea5647683%3C/grp_id%3E%3Coa%3E%3C/oa%3E%3Curl%3E%3C/url%3E&rft_id=info:oai/&rft_id=info:pmid/&rfr_iscdi=true