Effect of Magnification during Post Space Preparation on Root Cleanness and Fiber Post Bond Strength

• Published in: Brazilian dental journal 2019-10, Vol.30 (5), p.491-497
• Main Authors: Silva, Natércia Rezende da, Rodrigues, Monise de Paula, Bicalho, Aline Aredes, Deus, Raissa Albuquerque de, Soares, Priscilla Barbosa Ferreira, Soares, Carlos José
• Format: Article
• Language: English
• ISSN: 0103-6440; 1806-4760
• DOI: 10.1590/0103-6440201902662

Abstract The aim of this study was to evaluate the effect of magnification during post space preparation on root cleanness and on fiber post bond strength. Methods: Thirty human central upper incisors with similar root canal in size and shape were selected, decoronated to 15 mm and endodontically filled. The teeth were assigned into 3 groups (n=10), according to the method of magnification during post space preparation inspection: Control, using naked eye; loupe, using a dental surgical 3x magnifying glass; surgical microscope, using a 6x surgical microscope. The roots were scanned by using micro-CT before and after post space preparation for residue remnants evaluation. Fiber posts were cemented using self-adhesive resin cement (Rely X U200, 3M-ESPE). Two 1-mm-thick slices from the cervical, medium and apical thirds were submitted to a push-out test (PBS). Failures modes were classified. PBS data were analyzed by using two-way ANOVA with repeated measurement and the Tukey test. The significance level was set at 5%. The method of visualization had no effect on PBS (p=0.556). The cervical region had higher values than apical region irrespective of the inspection method (p=0.012). Adhesive failure between the resin cement and dentin was the prevalent failure mode for all groups. Micro-CT analysis showed no difference on root cleanness into the root canal after post space preparation. The use of magnification devices as loupe and microscope while performing post space do not improve the PBS and did not affect sealer remain of decoronated anterior teeth. Resumo Avaliar o efeito do método de visualização durante o preparo do espaço do pino sobre o remanescente de material obturador endodôntico e sobre a resistência adesiva do pino de fibra de vidro. Trinta incisivos centrais superiores humanos com canal radicular circular foram selecionados, foram desobstruídos a 15 mm e obturados. Os dentes foram divididos em 3 grupos (n=10), de acordo com o método de ampliação utilizado para inspeção do preparo: Controle, usando olho nu; lupa, usando uma lupa cirúrgica 3x cirúrgica; microscópio cirúrgico, usando um microscópio cirúrgico 6x. As raízes foram digitalizadas usando micro-CT antes e após a preparação do espaço para avaliação de resíduos remanescentes. Os pinos de fibra foram cimentados com cimento resinoso autoadesivo (RelyX U200, 3M-ESPE). Duas fatias de 1 mm de espessura dos terços cervical, médio e apical foram submetidas ao teste push-out (PBS). Os padrões de f