Modeling of Mechanical Performance from Concrete Made by Combining Iron Sand and Glass Powder Filler under Hot Water Curing Condition

• Published in: Mathematical Modelling of Engineering Problems 2022-04, Vol.9 (2), p.418-424
• Main Authors: Sugito, Sugito, Alisjahbana, Sofia W., Riyanto, Hery
• Format: Article
• Language: English
• ISSN: 2369-0739; 2369-0747
• DOI: 10.18280/mmep.090216

The proportions of the concrete are critical for obtaining a high-strength, high-quality product. Different concrete grades may support varying loads and have varying ratios. Therefore, the objectivity of this research is to study mechanical performance from concrete treated with iron sand, glass powder, and hot water curing. The level of iron sand and glass powder treatment added to the SNI concrete composition is 2% to 10%, 1% to 5%, (w/w), respectively. The curing time and temperature were applied between 1 hr to 4 hr and 301 K to 343 K. The compressive strength of the concrete was tested on 0, 1, 3, 7, and 28 days after molding using UTM with a combination of linear regression and response surface models for optimization. The addition of iron sand and glass powder to increase the best compressive strength was 10%, 2.45%, respectively. Iron sand treatment of 10% combined with glass powder filler 3.04% was predicted to give the best compressive strength of 32.50 MPa. The compressive strength value of this treatment was 21.78% higher than that of SNI concrete. Treat the curing temperature, curing time, and age of the concrete which gives the best compressive strength (28.33 MPa) with SNI concrete composition of 301 K, 4 days, and 28 days. This research shows that the addition of iron sand, glass powder, and hot water curing to the composition of SNI concrete can increase its compressive strength.