Effects of Briquetting and High Pyrolysis Temperature on Hydrolysis Lignin Char Properties and Reactivity in CO-CO2-N2 Conditions

• Published in: Minerals (Basel) 2021-02, Vol.11 (2), p.187
• Main Authors: Koskela, Aki, Heikkilä, Anne, Bergna, Davide, Salminen, Justin, Fabritius, Timo
• Format: Article
• Language: English
• ISSN: 2075-163X; 2075-163X
• DOI: 10.3390/min11020187

Carbonaceous reductants for pyrometallurgical applications are usually obtained from fossil-based sources. The most important properties of the reductants greatly depend on the application and the feeding of the reductant into the process. However, the mechanical strength, calorific value, fixed carbon content, and reactivity of the reductant are the properties that usually define the applicability of the reductant for different processes. The reactivity of the biochars is usually high in comparison to metallurgical coke, which may restrict the applicability of the biochar in reduction processes. One cause of the higher reactivity is the higher surface area of the biochars, which can be suppressed with agglomeration treatment, e.g., briquetting. In this work, hydrolysis lignin was used for slow pyrolysis experiments to produce biochars. The biochars were pyrolyzed in briquetted form and in as-received form at various temperatures. The reactivity values of the biochars were tested in dynamic reactivity tests in a CO-CO2-N2 gas atmosphere at temperatures of up to 1350 °C. It was found that the yield of the hydrolysis lignin char only decreased by 3.36 wt% when the pyrolysis temperature was elevated from 600 to 1200 °C, while a decrease in yield of 4.88 wt% occurred when the pyrolysis temperature was elevated from 450 to 600 °C. The mass loss of hydrolysis lignin biochar in the reactivity experiment in CO-CO2-N2 atmosphere was significantly decreased from 79.41 wt% to 56.80 wt% when the hydrolysis lignin was briquetted before the slow pyrolysis process and the temperature of the pyrolysis process was elevated from 600 to 1200 °C. This means that the mass loss of the material was suppressed by 22.61 wt% due to the higher pyrolysis temperature and briquetting process.