TEMPERATURE AND CRACK PATH DEVIATION EFFECTS ON FATIGUE CRACK GROWTH OF A NONCRYSTALLIZING RUBBER

This study presents an investigation of the displacement-driven fatigue behavior of a noncrystallizing rubber under various temperature conditions. Surprisingly, fatigue crack growth (FCG) experiments revealed an unexpected decrease in FCG rate and significant crack path deviations at higher tempera...

Full description

Saved in:
Bibliographic Details
Published in:Rubber chemistry and technology 2024-11
Main Authors: Chen, Pengshu, Li, Ziran, Wu, Ziheng, Shi, Zicheng, Wang, Yang
Format: Article
Language:English
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:This study presents an investigation of the displacement-driven fatigue behavior of a noncrystallizing rubber under various temperature conditions. Surprisingly, fatigue crack growth (FCG) experiments revealed an unexpected decrease in FCG rate and significant crack path deviations at higher temperatures. To explore this phenomenon, tear fracture experiments were conducted at various temperatures. Experimental observations revealed a notable decrease in fracture resistance at elevated temperatures. Subsequently, finite element methods were used to simulate the impact of crack path deviation on rubber fatigue, revealing that it reduces the tearing energy at the crack tip. Our investigation focused on the interaction between temperature and crack path deviation and its influence on rubber fatigue, with an emphasis on the critical role of crack path deviations at elevated temperatures in prolonging FCG.