Investigation of Microstructure and Magnetic Properties of CH4 Heat Treated Sr-Hexaferrite Powders during Re-Calcination Process

The microstructure and magnetic properties of methane (CH4) heat-treated Sr-hexaferrite powders during the re-calcination process were investigated and compared with the magnetic properties of conventionally synthesized Sr-hexaferrite powder. Gradual changes in the magnetic behavior of the produced...

Full description

Saved in:
Bibliographic Details
Published in:Magnetochemistry 2023-04, Vol.9 (4), p.103
Main Authors: Dehghan, Ramin, Seyyed Ebrahimi, Seyyed Ali, Lalegani, Zahra, Hamawandi, Bejan
Format: Article
Language:English
Subjects:
Citations: Items that this one cites
Items that cite this one
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:The microstructure and magnetic properties of methane (CH4) heat-treated Sr-hexaferrite powders during the re-calcination process were investigated and compared with the magnetic properties of conventionally synthesized Sr-hexaferrite powder. Gradual changes in the magnetic behavior of the produced powder in each re-calcination stage were investigated using magnetization curves obtained from the vibration sample magnetometry (VSM) technique. First, the initial Sr-hexaferrite powder was prepared by the conventional route. Then the powder was heat treated in a dynamic CH4 atmosphere in previously optimized conditions (temperature: 950 °C, gas flow rate:15 cc min−1 and time: 30 min), and finally, re-calcined in various temperatures from 200 to 1200 °C. By investigating the hysteresis loops, we found the transition temperature of soft to hard magnetic behavior to be 700 °C. The maximum ratio Mr/Ms was obtained at temperatures of 800–1100 °C. At 1100 °C, and despite the Sr-hexaferrite single phase, the magnetic behavior showed a multiphase behavior that was demonstrated by a kink in the hysteresis loop. Uniform magnetic behavior was observed only at 900 °C and 1000 °C. Although the ratio Mr/Ms was almost the same at these temperatures, the values of Mr and Ms at 1000 °C were almost double of 900 °C. At 1000 °C, the second quadrant of hysteresis curve had the maximum area. Therefore, 1000 °C was the optimum temperature for re-calcination after CH4 gas heat treatment in the optimized conditions. Due to the presence of a small amount of hematite soft phase at 1000 °C, the most probable reason for the exclusive properties of the optimized product may be the exchange coupling phenomenon between the hard Sr-hexaferrite phase and the impurity of the soft hematite phase.
ISSN:2312-7481
2312-7481
DOI:10.3390/magnetochemistry9040103