Incorporation of Dual-Stimuli Responsive Microgels in Nanofibrous Membranes for Cancer Treatment by Magnetic Hyperthermia

• Published in: Gels 2021-03, Vol.7 (1), p.28
• Main Authors: Gonçalves, Adriana, Almeida, Filipe V, Borges, João Paulo, Soares, Paula I P
• Format: Article
• Language: English
• Subjects: Acrylamide; Anticancer properties; Biocompatibility; Cancer therapies; Chemotherapy; Chitosan; colloidal electrospinning; Emulsion polymerization; Fever; Fourier transforms; Hyperthermia; Iron oxides; magnetic hyperthermia; magnetic nanoparticles; Membranes; microgel; Microgels; Modulus of elasticity; Morphology; Multifunctional materials; Nanoparticles; poly (N-isopropyl acrylamide); poly (vinyl pyrrolidone); Polymers; Solvents; Stiffness; Surfactants; Swelling ratio; Vibration
• ISSN: 2310-2861; 2310-2861
• DOI: 10.3390/gels7010028

The delivery of multiple anti-cancer agents holds great promise for better treatments. The present work focuses on developing multifunctional materials for simultaneous and local combinatory treatment: Chemotherapy and hyperthermia. We first produced hybrid microgels (MG), synthesized by surfactant-free emulsion polymerization, consisting of Poly ( -isopropyl acrylamide) (PNIPAAm), chitosan (40 wt.%), and iron oxide nanoparticles (NPs) (5 wt.%) as the inorganic component. PNIPAAm MGs with a hydrodynamic diameter of about 1 μm (in their swollen state) were successfully synthesized. With the incorporation of chitosan and NPs in PNIPAAm MG, a decrease in MG diameter and swelling capacity was observed, without affecting their thermosensitivity. We then sought to produce biocompatible and mechanically robust membranes containing these dual-responsive MG. To achieve this, MG were incorporated in poly (vinyl pyrrolidone) (PVP) fibers through colloidal electrospinning. The presence of NPs in MG decreases the membrane swelling ratio from 10 to values between 6 and 7, and increases the material stiffness, raising its Young modulus from 20 to 35 MPa. Furthermore, magnetic hyperthermia assay shows that PVP-MG-NP composites perform better than any other formulation, with a temperature variation of about 1 °C. The present work demonstrates the potential of using multifunctional colloidal membranes for magnetic hyperthermia and may in the future be used as an alternative treatment for cancer.