Combustion flame spray of 7YSZ powders followed by corrosion in molten salts of the coating

7YSZ coating was manufactured by combustion flame spray process of 7YSZ powders on MCrAlY substrate. Set parameters of combustion flame spray were used to build up an YSZ coating. Coating thickness in the range of 40-50 μm was obtained having microstructure of lamellar-splat morphology. Afterward, h...

Full description

Saved in:
Bibliographic Details
Published in:Journal of Asian Ceramic Societies 2021-04, Vol.9 (2), p.617-628
Main Authors: Mendoza, Melquisedec Vicente, Alvarez, Ricardo Cuenca, Juárez López, Fernando
Format: Article
Language:English
Subjects:
Combustion-flame-spray
corrosion
Yttria-stabilized-zirconia
Citations: Items that this one cites
Online Access:Get full text
Tags: Add Tag
No Tags, Be the first to tag this record!
Description
Summary:7YSZ coating was manufactured by combustion flame spray process of 7YSZ powders on MCrAlY substrate. Set parameters of combustion flame spray were used to build up an YSZ coating. Coating thickness in the range of 40-50 μm was obtained having microstructure of lamellar-splat morphology. Afterward, hot corrosion tests of the 7YSZ coating were performed in molten salts at 1050°C. Scanning electron microscopy and X-ray diffraction analysis was used to identify changes in the microstructure of the 7YSZ coating. It was identified as the main failure mechanism developed during spallation of YSZ coating.
ISSN:2187-0764
2187-0764
DOI:10.1080/21870764.2021.1905266